Controlling grain size and texture in MgeZneMn alloys from the interaction of recrystallization and precipitation
Date
2023
Abstract
The recrystallization behavior of extruded MgeZneMn alloys was systematically investigated under different aging treatment prior to extrusion. Electron backscattered diffraction analysis was used to explore the recrystallization mechanism and corresponding effects on the basal texture of alloys during extrusion. The results show that the primary coarse particles can effectively promote recrystallization nucleation. Moreover, the precipitation of nanoscale particles during the aging process play a role in pinning the grain boundaries. Therefore, after peak-aged treatment (16 h), the extruded Mg alloy obtains uniform and fine microstructure, showing good mechanical properties: the tensile yield strength, tensile strength, elongation, compressive yield strength, and tension-compression yield asymmetry were 298 MPa, 363 MPa, 26%, 260 MPa, and 0.87, respectively.
Supervisor
Description
Publisher
Elsevier
Citation
Journal of Materials Research and Technology, 2023, 21, pp. 1395-1407
Collections
Files
Funding code
Funding Information
This research was funded by Guangdong Major Project of Basic and Applied Basic Research (2020B0301030006), the National Natural Science Foundation of China (51971042, 51901028), the Fundamental Research Funds for the Central Universities Project (2021CDJQY-038), the Natural Science Foundation of Chongqing (cstc2021jcyj-msxmX0993) and the Chongqing Academician Special Fund (cstc2020yszx-jcyjX0001).