Understanding the thermal and dielectric response of organosolv and modified kraft lignin as a carbon fibre precursor

Download (1.41 MB)
journal contribution
posted on 2018-07-16, 11:00 authored by Mario Culebras, María Jesús Sanchis, Anne Beaucamp, M. Carsí, Baljinder K. Kandola, A.R. Horrocks, Gianmarco Panzettie, COLIN BIRKINSHAW, Maurice N. Collins
Understanding the thermal behaviour of lignin is crucial in order to realise its valorisation as an engineering polymer. Two hardwood lignins, organosolv (OSL) and chemically modified kraft lignin (ML) have been chosen to represent important classes of renewable and abundant raw material. The relationship between ionic mobility and viscosity in OSL and ML have been studied. The rheological results have been interpreted in terms of the competitive processes of thermal plasticisation and stiffening through crosslinking. Results show that with OSL crosslinking proceeds relatively rapidly, and this is consistent with its more reactive structure. Higher molecular weight (Mw) influenced the melt stability as cross-linking kinetics were reduced and this was attributed to the reduction of chain ends available for cross-linking reactions. Scanning calorimetry has shown that both materials are glassy and pass through the glass transition between 100 °C and 115 °C, with the higher molecular weight modified material having the slightly higher Tg. Both lignins show pronounced maxima in the Gramm-Schmidt plots for methane or methanol around 400°C. However, a significant difference between the materials is observed with the detection of a strong carbonyl peak in the evolution products of the ML, this is attributed to scission of the hydroxypropyl substituent present in the ML structure. The differences in the degradation processes are further reflected in the dielectric properties of the partially degraded materials where loss maxima occur at different temperatures, and show different degrees of frequency dependence. An important observation is the difference in conductivity, where higher values for OSL are attributed to cross-linking between adjacent benzene rings, whereas with the ML lower conductivity is associated with intrinsically less conductive intermolecular linkages. These results demonstrate that the thermal decomposition of the two lignins, follow significantly different paths at the molecular level. With the more reactive OSL it appears to be the case that there is a greater tendency to form direct ring to ring crosslinks and this is very significant for the properties of the intended end product.

Funding

Study on Aerodynamic Characteristics Control of Slender Body Using Active Flow Control Technique

Japan Society for the Promotion of Science

Find out more...

History

Publication

Green Chemistry; 20, pp. 4461-4772

Publisher

Royal Society of Chemistry

Note

peer-reviewed

Other Funding information

ERC, Spanish Ministry of Economy and Competitiveness

Rights

© 2018 Royal Society of Chemistry. Personal use of this material is permitted. Permission from Royal Society of Chemistry must be obtained for all other uses, in any current or future media, including reprinting/republishing this material for advertising or promotional purposes, creating new collective works, for resale or redistribution to servers or lists, or reuse of any copyrighted component of this work in other works.

Language

English

Usage metrics

    University of Limerick

    Categories

    No categories selected

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC